CLAM钢、EUROFER97钢与钨在HT-7托卡马克中辐照后的表面分析Surface analysis of CLAM steel, EUROFER97 steel and W irradiated in HT-7 Tokamak
李强,黄群英,郁金南,李建刚,吴宜灿,何晓雄
摘要(Abstract)：
两种低活化马氏体钢(CLAM、EUROFER97)以及钨被放入HT-7托卡马克的刮削层中,以研究托卡马克装置中高温等离子体与低活化马氏体钢和钨表面的相互作用。通过SEM装置观察,发现某些样品的表面形貌发生了很大变化。低活化马氏体钢的表面起泡比较密集,钨的表面起泡比较稀少,且直径较大。在一些样品的表面,还观察到了等离子体灰尘以及明显的被等离子体冲击后的痕迹。另外,XPS分析发现样品表面的某些元素成分也发生了变化,而且处在托卡马克装置中不同位置处的样品,其表面硅的含量呈现出明显的规律性。
关键词(KeyWords)： 低活化马氏体钢CLAM;EUROFER97;钨;HT-7托卡马克;辐照;表面分析
基金项目(Foundation): 国家自然科学基金资助项目(10375067);; 中国科学院知识创新工程资助项目
作者(Author): 李强,黄群英,郁金南,李建刚,吴宜灿,何晓雄
参考文献(References)：
- [1] Hishnuma A, et al. Current status and future R & D for reduced-activation ferritic/martensitic steels [J]. J, Nucl Mater, 1998, 258~263:193-204．
- [2] Klueh RL, et al. Ferritic/martensitic steels-overview of recent results [J]. J Nucl Mater, 2002, 307-311:455-465．
- [3] Wu YC. et al. The fusion-driven hybrid system and its material selection [J]. J Nucl Mater, 2002, 307-311; 1 629-1 636．
- [4] 黄群英,等.聚变堆低活化马氏体钢发展综述[J].核科学与工程,2004,24(1) :56～64．
- [5] Tsuzuki K, et al. Recent activities on the compatibility of the ferritic steel wall with the plasma in the JFT-2M tokamak [J]. J Nucl Mater, 2002, 307-311:1 386-1 390．
- [6] Janeschitz G, et al. The ITER divertor concept [J]. J. Nucl Mater, 1995, 220-222:73-88．
- [7] Naoaki yoshida. Review of recent works in development and evaluation of high-z plasma facing materials [J]. J Nucl Mater, 1999, 266-269:191-206．
- [8] Krieger K, et al. Plasma-wall interaction at the ASDEX Upgrade tungsten heat shield [J]. Fusion Eng Des, 2001, 56-57:189-193．
- [9] Neu R, et al. Impurity behaviour in the ASDEX Upgrade divertor tokamak with large area tungsten walls [J]. Plasma Phys Control Fusion, 2002, 44:811-826．
- [10] Maier H, et al. J Nucl Mater, 2002, 307-311:116-120．
- [11] Krieger K, Development of tungsten coated first wall and high heat flux components for application in ASDEX Upgrade[J]. J Nucl Mater, 2003, 313-316:327-337．
- [12] Lucon E, Mechanical tests on two batches of oxide dispersion strengthened RAFM steel (EUROFER97) [J]. Fus. Eng. Des, et al. Erosion and migration of tungsten employed at the main Upgrade [J]. Chamber first wall of ASDEX, 2002, 61~62:683~689．
- [13] Evans J H, An interbubble fracture machanism of blister formation on helium-irradiated metals [J]. J Nucl Mater, 1977,68: 129-140．
- [14] EerNisse E P, et al. Role of integrated lated stress in surface deformation of He-implanted surfaces [J]. J Ap-pl Phys, 1977, 48:9-17．
- [15] Yu J, et al. The blistering of 316L stainless steel irradiated with energetic alpha particles at 500℃ [J]. J Nucl Mater. 1992, 191-194:818-821．
- [16] Ye M Y, et al. Blister formation on tungsten surface under low energy and high flux hydrogen plasma irradi-tion in NAGDIS-I [J]. J. Nucl. Mater, 2003, 313-316:72-76．